Physicochemical properties of WO_x/ZrO₂ catalysts for palmitic acid esterification

A series of WO_x/ZrO₂ with various tungsten loadings was prepared via incipient-wetness impregnation of zirconium hydroxide. The resulting thermally processed materials were characterised by XRD, XPS, porosimetry, NH₃-TPD and pyridine FTIR spectroscopy to elucidate their composition, morphology and acidity, and subsequently tested in the esterification of palmitic acid with methanol. Catalytic performance was strongly dependent upon calcination temperature and W surface density. Esterification activity increased with increasing surface W density, reaching a maximum at 8.9Wnm^-2 corresponding to near monolayer coverage. Subsequent growth of crystalline WO₃ lowered activity, consistent with a decrease in the density of active surface sites. Calcination temperatures as high as 800°C increased surface acidity and hence catalytic activity. The formation of polymeric tungstate species on zirconia is necessary to generate the Brönsted acid sites responsible for palmitic acid esterification under mild conditions. © 2014 Elsevier B.V.